DSpace
 

EPrints@IIT Delhi >
Faculty Research Publicatons  >
Physics >

Please use this identifier to cite or link to this item: http://eprint.iitd.ac.in/handle/2074/1370

Full metadata record

DC FieldValueLanguage
dc.contributor.authorRoy, Somnath C-
dc.contributor.authorBhatnagar, M C-
dc.contributor.authorSharma, G L-
dc.contributor.authorManchanda, R-
dc.contributor.authorBalakrishnan, V R-
dc.date.accessioned2006-02-22T03:43:22Z-
dc.date.available2006-02-22T03:43:22Z-
dc.date.issued2004-
dc.identifier.citationCeramics International, 30(8), 2283-2287en
dc.identifier.urihttp://eprint.iitd.ac.in/dspace/handle/2074/1370-
dc.description.abstract(Ba0.5Sr0.5)TiO3 thin films have been deposited by sol–gel technique and the effect of pre-sintering temperature on the structural and dielectric properties has been studied. The sol was prepared from barium acetate and strontium acetate powders by dissolving them in acetic acid; while titanium isopropoxide was used as titanium source. Acetyl acetone, 2-methoxyethanol, and formamide were used as chelating agent, diluting reagent, and for getting crack free films, respectively. Two sets of films were prepared; one set pre-sintered at 400 °C while the other one at 600 °C. In all the cases, the final sintering temperature was kept fixed at 700 °C for 2 h. These films were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), dielectric constant, and loss measurements and AC conductivity studies. It has been found that with an increase in the pre-sintering temperature from 400 to 600 °C, the dielectric constant increases from 225 to 383 (measured at 100 kHz); whereas, the loss tangent remains nearly constant at 0.03–0.05. The XRD results show better crystallinity and enhanced grain growth in case of films pre-sintered at 600 °C. The FTIR spectra reveals that there is significant removal of organic materials in films with higher pre-sintering temperature as compared to that with lower pre-sintering temperature. The AC conductivity studies show a decrease in the frequency exponent ‘s’ with an increase in the pre-sintering temperature which has been correlated with the reduction in oxygen vacancy densities in the sample with higher pre-sintering temperature.en
dc.format.extent567722 bytes-
dc.format.mimetypeapplication/pdf-
dc.language.isoenen
dc.subjectDielectric propertiesen
dc.subjectSol–gelen
dc.subjectBarium strontium titanateen
dc.subjectAC conductivityen
dc.titleEffect of pre-sintering temperature on the structural and dielectric properties of (Ba0.5Sr0.5)TiO3 thin films deposited by sol–gel techniqueen
dc.typeArticleen
Appears in Collections:Physics

Files in This Item:

File Description SizeFormat
royeff2004.pdf554.42 kBAdobe PDFView/Open
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback