DSpace
 

EPrints@IIT Delhi >
Faculty Research Publicatons  >
Textile Technology >

Please use this identifier to cite or link to this item: http://eprint.iitd.ac.in/handle/2074/894

Full metadata record

DC FieldValueLanguage
dc.contributor.authorBajaj, P-
dc.contributor.authorSreekumar, T V-
dc.contributor.authorSen, K-
dc.date.accessioned2005-10-18T05:13:05Z-
dc.date.available2005-10-18T05:13:05Z-
dc.date.issued2001-
dc.identifier.citationPolymer, 42(4), 1707–1718en
dc.identifier.urihttp://eprint.iitd.ac.in/dspace/handle/2074/894-
dc.description.abstractThe effect of comonomers, methacrylic (MAA 3–6 mol%) and itaconic acid (IA 2–3 mol%) on the glass transition temperature, Tg, hydration melting and thermo-oxidative stabilization of acrylonitrile copolymers has been studied by differential scanning calorimetry (DSC). While, two Tg‘s were observed, near 70 and 1408C, for PAN homopolymer, copolymers showed another baseline shift below 708C. The melting point, Tm, of PAN and copolymer, P(AN/IA) containing 3.2 mol% of IA, has been reduced to 186 and 1588C, respectively, in high-pressure DSC. The copolymers showed two distinct melting peaks in the first heating cycle, but the melt on subsequent cooling exhibited a single exotherm due to crystallization. The melting point of IA copolymer (1588C) was found to be lower than that of MAA copolymer (1648C) and PAN homopolymer (1868C). Tm further decreases with increase in the comonomer content. In the second heating cycle, observed Tm is higher than that noted in the first heating run, indicating some amount of physical transformations. The enthalpy of fusion, DHf decreases with the incorporation of comonomers, e.g. it is maximum for PAN homopolymer (57.8 J g21) and minimum for P(AN/IA) copolymer (26 J g21) having 3.2 mol% of IA content. The lower entropy of fusion (DSf) of copolymers indicates that they are less mobile in the molten state. DSC of copolymers run in air atmosphere, at a heating rate of 108C min21, shows a broader exotherm compared to homopolymer. But, the broadening of exotherm seems to be more in P(AN/IA) polymers than P(AN/MAA) and the onset of cyclization shifts to a lower temperature as compared to PAN. The activation energy of nitrile cyclization, Ea, for PAN is found to be 30 kcal mol21. For copolymer P(AN/IA), IA = 3.2 mol%, Ea is 18 kcal mol21.en
dc.format.extent345832 bytes-
dc.format.mimetypeapplication/pdf-
dc.language.isoenen
dc.subjectPANen
dc.subjectAcrylonitrile vinyl acid copolymersen
dc.subjectHigh-pressure DSCen
dc.titleThermal behaviour of acrylonitrile copolymers having methacrylic and itaconic acid comonomersen
dc.typeArticleen
Appears in Collections:Textile Technology

Files in This Item:

File Description SizeFormat
bajajthe2001.pdf337.73 kBAdobe PDFView/Open
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback