Electrical properties of PZT thin films grown by sol–gel and PLD using a seed layer
Lead Zirconate Titanate (PZT) thin films (with molar ratio of Zr:Ti
Polymeric citrate precursor route to the synthesis of the high dielectric constant oxide, CaCu3Ti4O12
Using citric acid and ethylene glycol, a polymeric precursor of the above compound was obtained at low temperatures (135 °C) which on subsequent heat treatments led to pure CaCu3Ti4O12 at 1000 °C. On sintering further at ...
Synthesis and microwave dielectric properties of Sr3Zn1−xMgxNb2O9 phases
Oxides of the type, Sr3Zn1−xMgxNb2O9 (0≤x≤1) have been obtained by the ceramic method. These oxides crystallize in the hexagonal cell corresponding to ordered triple perovskites. Sintered disks show nearly frequency-independent ...
Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9: synthesis, structural and dielectric studies
Oxides of the families Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 were obtained by the solid state reaction route at 1573 K and were found to crystallize in the disordered (cubic) perovskite structure. In Ba3ZnTa2−xNbxO9 and ...
Polymeric citrate precursor route to the synthesis of nano-sized barium lead titanates
Monophasic oxides of the formula, Ba1−xPbxTiO3 (0≤x≤1.0) were obtained at temperatures close to 500 °C from polymeric precursors formed using citric acid and ethylene glycol. These oxides were found to be tetragonal for ...
New double perovskites having low dielectric loss:LaBaZnTaO6, LaSrZnNbO6, and Ba2Zn0.5Ti0.5TaO6
Oxides of the type LaBaZnTaO6 and LaSrZnNbO6 have been synthesized by the solid-state method at 1100°C. Ba2Zn0.5Ti0.5TaO6 was synthesized by the molten salt method (using NaCl–KCl as flux), the solid-state method yielding ...
Dielectric properties of lead zirconium titanates with nanometer size grains synthesized by the citrate precursor route
Monophasic oxides of the formula, PbZrxTi1−xO3 (0.0≤x≤0.75) were obtained at temperatures close to 500 °C from polymeric precursors formed using citric acid and ethylene glycol. The oxides were found to be tetragonal for ...
Synthesis and dielectric properties of magnesium niobate -magnesium tantalate solid solutions
Monophasic Oxides of the type MgNb2−xTaxO6 (0 ≤ x ≤ 2) have been synthesized by solid-state reactions using Mg(NO3)2·6H2O as the source of Mg. The oxides crystallize in the orthorhombic columbite structure till X = 1.75 ...
(La0.4Ba0.4Ca0.2)(Mn0.4Ti0.6)O3: A new titano-manganate with a high dielectric constant and antiferromagnetic interactions
A new perovskite-based titano-manganate, (La0.4Ba0.4Ca0.2)(Mn0.4Ti0.6)O3, has been prepared by the ceramic route at 1100°C. This oxide was found to possess the cubic perovskite structure with ‘a’=3.9477(23) Å (space group ...
Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 (0≤x≤1): synthesis, structure and dielectric properties
Oxides belonging to the families Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 were synthesized by the solid state reaction route. Sintering temperatures of 1300°C led to oxides with disordered (cubic) perovskite structure. However, ...