Dielectric properties of lead zirconium titanates with nanometer size grains synthesized by the citrate precursor route
(2003)
Monophasic oxides of the formula, PbZrxTi1−xO3 (0.0≤x≤0.75) were obtained at temperatures close to 500 °C from polymeric precursors formed using citric acid and ethylene glycol. The oxides were found to be tetragonal for ...
(La0.4Ba0.4Ca0.2)(Mn0.4Ti0.6)O3: A new titano-manganate with a high dielectric constant and antiferromagnetic interactions
(2004)
A new perovskite-based titano-manganate, (La0.4Ba0.4Ca0.2)(Mn0.4Ti0.6)O3, has been prepared by the ceramic route at 1100°C. This oxide was found to possess the cubic perovskite structure with ‘a’=3.9477(23) Å (space group ...
Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 (0≤x≤1): synthesis, structure and dielectric properties
(2002)
Oxides belonging to the families Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 were synthesized by the solid state reaction route. Sintering temperatures of 1300°C led to oxides with disordered (cubic) perovskite structure. However, ...
Synthesis and microwave dielectric properties of Sr3Zn1−xMgxNb2O9 phases
(2002)
Oxides of the type, Sr3Zn1−xMgxNb2O9 (0≤x≤1) have been obtained by the ceramic method. These oxides crystallize in the hexagonal cell corresponding to ordered triple perovskites. Sintered disks show nearly frequency-independent ...
Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9: synthesis, structural and dielectric studies
(2000)
Oxides of the families Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 were obtained by the solid state reaction route at 1573 K and were found to crystallize in the disordered (cubic) perovskite structure. In Ba3ZnTa2−xNbxO9 and ...
Polymeric citrate precursor route to the synthesis of nano-sized barium lead titanates
(2003)
Monophasic oxides of the formula, Ba1−xPbxTiO3 (0≤x≤1.0) were obtained at temperatures close to 500 °C from polymeric precursors formed using citric acid and ethylene glycol. These oxides were found to be tetragonal for ...